Annealed 300 Maraging Steel vs. ASTM A387 Grade 22 Class 1
Both annealed 300 maraging steel and ASTM A387 grade 22 class 1 are iron alloys. Both are furnished in the annealed condition. They have 68% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is annealed 300 maraging steel and the bottom bar is ASTM A387 grade 22 class 1.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 18 | |
| 21 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 74 |
| Shear Strength, MPa | 640 | |
| 300 |
| Tensile Strength: Ultimate (UTS), MPa | 1030 | |
| 480 |
| Tensile Strength: Yield (Proof), MPa | 760 | |
| 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 260 |
| Melting Completion (Liquidus), °C | 1480 | |
| 1470 |
| Melting Onset (Solidus), °C | 1430 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 34 | |
| 3.8 |
| Density, g/cm3 | 8.2 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 5.1 | |
| 1.7 |
| Embodied Energy, MJ/kg | 68 | |
| 23 |
| Embodied Water, L/kg | 150 | |
| 58 |
Common Calculations
| PREN (Pitting Resistance) | 16 | |
| 5.6 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 170 | |
| 85 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1490 | |
| 140 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 23 | |
| 24 |
| Strength to Weight: Axial, points | 35 | |
| 17 |
| Strength to Weight: Bending, points | 28 | |
| 17 |
| Thermal Shock Resistance, points | 31 | |
| 14 |
Alloy Composition
| Aluminum (Al), % | 0.050 to 0.15 | |
| 0 |
| Boron (B), % | 0 to 0.0030 | |
| 0 |
| Calcium (Ca), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 0 | |
| 2.0 to 2.5 |
| Cobalt (Co), % | 8.5 to 9.5 | |
| 0 |
| Iron (Fe), % | 65 to 68.4 | |
| 95.1 to 96.8 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 4.6 to 5.2 | |
| 0.9 to 1.1 |
| Nickel (Ni), % | 18 to 19 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.025 |
| Titanium (Ti), % | 0.5 to 0.8 | |
| 0 |
| Zirconium (Zr), % | 0 to 0.020 | |
| 0 |