Automotive Grey Cast Iron vs. EN 1.4594 Stainless Steel
Both automotive grey cast iron and EN 1.4594 stainless steel are iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is automotive grey cast iron and the bottom bar is EN 1.4594 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 200 |
| Elongation at Break, % | 9.6 to 14 | |
| 11 to 17 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 69 to 70 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 140 to 290 | |
| 1020 to 1170 |
| Tensile Strength: Yield (Proof), MPa | 94 to 200 | |
| 810 to 1140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 to 280 | |
| 280 |
| Melting Completion (Liquidus), °C | 1380 to 1390 | |
| 1450 |
| Melting Onset (Solidus), °C | 1340 to 1350 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 470 |
| Thermal Conductivity, W/m-K | 41 to 43 | |
| 16 |
| Thermal Expansion, µm/m-K | 12 to 14 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 to 7.6 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 to 9.1 | |
| 2.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 to 3.0 | |
| 15 |
| Density, g/cm3 | 7.5 to 7.6 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.5 to 1.7 | |
| 3.2 |
| Embodied Energy, MJ/kg | 21 to 24 | |
| 45 |
| Embodied Water, L/kg | 44 to 51 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 18 to 25 | |
| 110 to 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 25 to 110 | |
| 1660 to 3320 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 5.2 to 11 | |
| 36 to 41 |
| Strength to Weight: Bending, points | 8.0 to 13 | |
| 29 to 31 |
| Thermal Diffusivity, mm2/s | 11 to 12 | |
| 4.4 |
| Thermal Shock Resistance, points | 4.2 to 8.6 | |
| 34 to 39 |