Baria-alkali-silica Glass vs. Ferrite
Baria-alkali-silica glass belongs to the glass and glass-ceramics classification, while ferrite belongs to the oxide-based engineering ceramics. There are 7 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is baria-alkali-silica glass and the bottom bar is ferrite.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 3.0 | |
| 4.7 to 4.8 |
| Elastic (Young's, Tensile) Modulus, GPa | 80 | |
| 120 to 140 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 12 | |
| 1.0 to 1.5 |
| Flexural Strength, MPa | 34 | |
| 120 to 150 |
| Stiffness to Weight: Axial, points | 15 | |
| 15 to 16 |
| Stiffness to Weight: Bending, points | 48 | |
| 35 to 36 |
| Thermal Expansion, µm/m-K | 9.5 | |
| 8.0 to 9.3 |