C355.0 Aluminum vs. AWS E307

C355.0 aluminum belongs to the aluminum alloys classification, while AWS E307 belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C355.0 aluminum and the bottom bar is AWS E307.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
200
Elongation at Break, % 2.7 to 3.8
34
Poisson's Ratio 0.33
0.28
Shear Modulus, GPa 26
78
Tensile Strength: Ultimate (UTS), MPa 290 to 310
660

Thermal Properties

Latent Heat of Fusion, J/g 470
290
Melting Completion (Liquidus), °C 620
1420
Melting Onset (Solidus), °C 570
1370
Specific Heat Capacity, J/kg-K 900
480
Thermal Conductivity, W/m-K 150
15
Thermal Expansion, µm/m-K 22
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 39
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 130
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
17
Density, g/cm3 2.7
7.8
Embodied Carbon, kg CO2/kg material 8.0
3.5
Embodied Energy, MJ/kg 150
49
Embodied Water, L/kg 1120
160

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 51
25
Strength to Weight: Axial, points 30 to 32
24
Strength to Weight: Bending, points 36 to 37
22
Thermal Diffusivity, mm2/s 60
4.1
Thermal Shock Resistance, points 13 to 14
17

Alloy Composition

Aluminum (Al), % 91.7 to 94.1
0
Carbon (C), % 0
0.040 to 0.14
Chromium (Cr), % 0
18 to 21.5
Copper (Cu), % 1.0 to 1.5
0 to 0.75
Iron (Fe), % 0 to 0.2
59.6 to 69.2
Magnesium (Mg), % 0.4 to 0.6
0
Manganese (Mn), % 0 to 0.1
3.3 to 4.8
Molybdenum (Mo), % 0
0.5 to 1.5
Nickel (Ni), % 0
9.0 to 10.7
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 4.5 to 5.5
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Titanium (Ti), % 0 to 0.2
0
Zinc (Zn), % 0 to 0.1
0
Residuals, % 0 to 0.15
0