C355.0 Aluminum vs. Grade N12MV Nickel

C355.0 aluminum belongs to the aluminum alloys classification, while grade N12MV nickel belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is C355.0 aluminum and the bottom bar is grade N12MV nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 70
220
Elongation at Break, % 2.7 to 3.8
6.8
Fatigue Strength, MPa 76 to 84
130
Poisson's Ratio 0.33
0.31
Shear Modulus, GPa 26
84
Tensile Strength: Ultimate (UTS), MPa 290 to 310
600
Tensile Strength: Yield (Proof), MPa 200 to 230
310

Thermal Properties

Latent Heat of Fusion, J/g 470
320
Maximum Temperature: Mechanical, °C 170
900
Melting Completion (Liquidus), °C 620
1620
Melting Onset (Solidus), °C 570
1570
Specific Heat Capacity, J/kg-K 900
390
Thermal Expansion, µm/m-K 22
10

Otherwise Unclassified Properties

Base Metal Price, % relative 9.5
75
Density, g/cm3 2.7
9.2
Embodied Carbon, kg CO2/kg material 8.0
16
Embodied Energy, MJ/kg 150
200
Embodied Water, L/kg 1120
260

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 7.5 to 9.8
34
Resilience: Unit (Modulus of Resilience), kJ/m3 290 to 380
220
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 51
22
Strength to Weight: Axial, points 30 to 32
18
Strength to Weight: Bending, points 36 to 37
17
Thermal Shock Resistance, points 13 to 14
19

Alloy Composition

Aluminum (Al), % 91.7 to 94.1
0
Carbon (C), % 0
0 to 0.12
Chromium (Cr), % 0
0 to 1.0
Copper (Cu), % 1.0 to 1.5
0
Iron (Fe), % 0 to 0.2
4.0 to 6.0
Magnesium (Mg), % 0.4 to 0.6
0
Manganese (Mn), % 0 to 0.1
0 to 1.0
Molybdenum (Mo), % 0
26 to 30
Nickel (Ni), % 0
60.2 to 69.8
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 4.5 to 5.5
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Titanium (Ti), % 0 to 0.2
0
Vanadium (V), % 0
0.2 to 0.6
Zinc (Zn), % 0 to 0.1
0
Residuals, % 0 to 0.15
0