C355.0 Aluminum vs. R56401 Titanium
C355.0 aluminum belongs to the aluminum alloys classification, while R56401 titanium belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C355.0 aluminum and the bottom bar is R56401 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 110 |
| Elongation at Break, % | 2.7 to 3.8 | |
| 9.1 |
| Fatigue Strength, MPa | 76 to 84 | |
| 480 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 26 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 290 to 310 | |
| 940 |
| Tensile Strength: Yield (Proof), MPa | 200 to 230 | |
| 850 |
Thermal Properties
| Latent Heat of Fusion, J/g | 470 | |
| 410 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 340 |
| Melting Completion (Liquidus), °C | 620 | |
| 1610 |
| Melting Onset (Solidus), °C | 570 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 560 |
| Thermal Conductivity, W/m-K | 150 | |
| 7.1 |
| Thermal Expansion, µm/m-K | 22 | |
| 9.6 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 39 | |
| 1.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 130 | |
| 2.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 36 |
| Density, g/cm3 | 2.7 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 8.0 | |
| 38 |
| Embodied Energy, MJ/kg | 150 | |
| 610 |
| Embodied Water, L/kg | 1120 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 7.5 to 9.8 | |
| 83 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 to 380 | |
| 3440 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 51 | |
| 35 |
| Strength to Weight: Axial, points | 30 to 32 | |
| 59 |
| Strength to Weight: Bending, points | 36 to 37 | |
| 48 |
| Thermal Diffusivity, mm2/s | 60 | |
| 2.9 |
| Thermal Shock Resistance, points | 13 to 14 | |
| 67 |
Alloy Composition
| Aluminum (Al), % | 91.7 to 94.1 | |
| 5.5 to 6.5 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Copper (Cu), % | 1.0 to 1.5 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.012 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 to 0.25 |
| Magnesium (Mg), % | 0.4 to 0.6 | |
| 0 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.13 |
| Silicon (Si), % | 4.5 to 5.5 | |
| 0 |
| Titanium (Ti), % | 0 to 0.2 | |
| 88.5 to 91 |
| Vanadium (V), % | 0 | |
| 3.5 to 4.5 |
| Zinc (Zn), % | 0 to 0.1 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 |