Class 3 Tungsten vs. S46910 Stainless Steel
Class 3 tungsten belongs to the otherwise unclassified metals classification, while S46910 stainless steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is class 3 tungsten and the bottom bar is S46910 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 270 | |
| 200 |
| Elongation at Break, % | 3.4 | |
| 2.2 to 11 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Rockwell C Hardness | 30 | |
| 29 to 63 |
| Shear Modulus, GPa | 100 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 830 | |
| 680 to 2470 |
| Tensile Strength: Yield (Proof), MPa | 580 | |
| 450 to 2290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 280 |
| Specific Heat Capacity, J/kg-K | 120 | |
| 470 |
| Thermal Expansion, µm/m-K | 4.5 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 15 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 4.1 |
| Embodied Energy, MJ/kg | 360 | |
| 55 |
| Embodied Water, L/kg | 150 | |
| 140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 25 | |
| 48 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 630 | |
| 510 to 4780 |
| Stiffness to Weight: Axial, points | 9.6 | |
| 14 |
| Stiffness to Weight: Bending, points | 14 | |
| 24 |
| Strength to Weight: Axial, points | 15 | |
| 24 to 86 |
| Strength to Weight: Bending, points | 13 | |
| 22 to 51 |
| Thermal Shock Resistance, points | 49 | |
| 23 to 84 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.15 to 0.5 |
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 11 to 13 |
| Copper (Cu), % | 0 | |
| 1.5 to 3.5 |
| Iron (Fe), % | 0 | |
| 65 to 76 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 3.0 to 5.0 |
| Nickel (Ni), % | 0 | |
| 8.0 to 10 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0 to 0.7 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0.5 to 1.2 |
| Tungsten (W), % | 95 | |
| 0 |
| Residuals, % | 5.0 | |
| 0 |