Commercially Pure Silver vs. Grade FDSiCrV Steel

Commercially pure silver belongs to the otherwise unclassified metals classification, while grade FDSiCrV steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is commercially pure silver and the bottom bar is grade FDSiCrV steel.

Commercially Pure Silver Grade FDSiCrV Spring Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		71
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.37
Poisson's Ratio		0.29

Shear Modulus, GPa		26
Shear Modulus, GPa		80

Tensile Strength: Ultimate (UTS), MPa		190 to 340
Tensile Strength: Ultimate (UTS), MPa		2100

Thermal Properties

Latent Heat of Fusion, J/g		110
Latent Heat of Fusion, J/g		270

Melting Completion (Liquidus), °C		960
Melting Completion (Liquidus), °C		1440

Melting Onset (Solidus), °C		960
Melting Onset (Solidus), °C		1400

Specific Heat Capacity, J/kg-K		240
Specific Heat Capacity, J/kg-K		480

Thermal Conductivity, W/m-K		420
Thermal Conductivity, W/m-K		47

Thermal Expansion, µm/m-K		20
Thermal Expansion, µm/m-K		13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS		100
Electrical Conductivity: Equal Volume, % IACS		7.4

Electrical Conductivity: Equal Weight (Specific), % IACS		87
Electrical Conductivity: Equal Weight (Specific), % IACS		8.6

Otherwise Unclassified Properties

Density, g/cm³		10
Density, g/cm³		7.7

Common Calculations

Stiffness to Weight: Axial, points		3.8
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		13
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		4.9 to 8.9
Strength to Weight: Axial, points		75

Strength to Weight: Bending, points		6.9 to 10
Strength to Weight: Bending, points		47

Thermal Diffusivity, mm²/s		170
Thermal Diffusivity, mm²/s		13

Thermal Shock Resistance, points		9.5 to 17
Thermal Shock Resistance, points		63

Alloy Composition

Carbon (C), %		0
Carbon (C), %		0.5 to 0.7

Chromium (Cr), %		0
Chromium (Cr), %		0.5 to 1.0

Copper (Cu), %		0
Copper (Cu), %		0 to 0.12

Iron (Fe), %		0
Iron (Fe), %		96 to 97.8

Manganese (Mn), %		0
Manganese (Mn), %		0.4 to 0.9

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0
Silicon (Si), %		1.2 to 1.7

Silver (Ag), %		99.9 to 100
Silver (Ag), %		0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.025

Vanadium (V), %		0
Vanadium (V), %		0.1 to 0.25

Residuals, %		0 to 0.1
Residuals, %		0