Commercially Pure Silver vs. SAE-AISI M43 Steel
Commercially pure silver belongs to the otherwise unclassified metals classification, while SAE-AISI M43 steel belongs to the iron alloys. There are 17 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is commercially pure silver and the bottom bar is SAE-AISI M43 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 200 |
| Poisson's Ratio | 0.37 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 190 to 340 | |
| 810 to 2290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 110 | |
| 270 |
| Melting Completion (Liquidus), °C | 960 | |
| 1550 |
| Melting Onset (Solidus), °C | 960 | |
| 1500 |
| Specific Heat Capacity, J/kg-K | 240 | |
| 450 |
| Thermal Conductivity, W/m-K | 420 | |
| 19 |
| Thermal Expansion, µm/m-K | 20 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 8.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.8 | |
| 14 |
| Stiffness to Weight: Bending, points | 13 | |
| 24 |
| Strength to Weight: Axial, points | 4.9 to 8.9 | |
| 27 to 77 |
| Strength to Weight: Bending, points | 6.9 to 10 | |
| 24 to 47 |
| Thermal Diffusivity, mm2/s | 170 | |
| 5.3 |
| Thermal Shock Resistance, points | 9.5 to 17 | |
| 25 to 71 |
Alloy Composition
| Carbon (C), % | 0 | |
| 1.2 to 1.3 |
| Chromium (Cr), % | 0 | |
| 3.5 to 4.3 |
| Cobalt (Co), % | 0 | |
| 7.8 to 8.8 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 | |
| 70.8 to 76 |
| Manganese (Mn), % | 0 | |
| 0.2 to 0.4 |
| Molybdenum (Mo), % | 0 | |
| 7.5 to 8.5 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.65 |
| Silver (Ag), % | 99.9 to 100 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 2.3 to 3.0 |
| Vanadium (V), % | 0 | |
| 1.5 to 1.8 |
| Residuals, % | 0 to 0.1 | |
| 0 |