Commercially Pure Silver vs. C54400 Bronze
Commercially pure silver belongs to the otherwise unclassified metals classification, while C54400 bronze belongs to the copper alloys. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is commercially pure silver and the bottom bar is C54400 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 71 | |
| 110 |
| Poisson's Ratio | 0.37 | |
| 0.34 |
| Shear Modulus, GPa | 26 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 190 to 340 | |
| 330 to 720 |
Thermal Properties
| Latent Heat of Fusion, J/g | 110 | |
| 190 |
| Melting Completion (Liquidus), °C | 960 | |
| 1000 |
| Melting Onset (Solidus), °C | 960 | |
| 930 |
| Specific Heat Capacity, J/kg-K | 240 | |
| 370 |
| Thermal Conductivity, W/m-K | 420 | |
| 86 |
| Thermal Expansion, µm/m-K | 20 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 100 | |
| 19 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 87 | |
| 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 8.9 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.8 | |
| 6.8 |
| Stiffness to Weight: Bending, points | 13 | |
| 18 |
| Strength to Weight: Axial, points | 4.9 to 8.9 | |
| 10 to 22 |
| Strength to Weight: Bending, points | 6.9 to 10 | |
| 12 to 20 |
| Thermal Diffusivity, mm2/s | 170 | |
| 26 |
| Thermal Shock Resistance, points | 9.5 to 17 | |
| 12 to 26 |
Alloy Composition
| Copper (Cu), % | 0 | |
| 85.4 to 91.5 |
| Iron (Fe), % | 0 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 3.5 to 4.5 |
| Phosphorus (P), % | 0 | |
| 0.010 to 0.5 |
| Silver (Ag), % | 99.9 to 100 | |
| 0 |
| Tin (Sn), % | 0 | |
| 3.5 to 4.5 |
| Zinc (Zn), % | 0 | |
| 1.5 to 4.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |