EN 1.0034 Steel vs. AISI 414 Stainless Steel
Both EN 1.0034 steel and AISI 414 stainless steel are iron alloys. They have 85% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.0034 steel and the bottom bar is AISI 414 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 9.0 to 32 | |
| 17 |
| Fatigue Strength, MPa | 140 to 170 | |
| 430 to 480 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 76 |
| Shear Strength, MPa | 220 to 230 | |
| 550 to 590 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 380 | |
| 900 to 960 |
| Tensile Strength: Yield (Proof), MPa | 180 to 280 | |
| 700 to 790 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 750 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1440 |
| Melting Onset (Solidus), °C | 1420 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 53 | |
| 25 |
| Thermal Expansion, µm/m-K | 12 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 2.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 2.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 8.0 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.1 |
| Embodied Energy, MJ/kg | 18 | |
| 29 |
| Embodied Water, L/kg | 45 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 31 to 95 | |
| 140 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 84 to 210 | |
| 1260 to 1590 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 12 to 13 | |
| 32 to 34 |
| Strength to Weight: Bending, points | 14 to 15 | |
| 27 to 28 |
| Thermal Diffusivity, mm2/s | 14 | |
| 6.7 |
| Thermal Shock Resistance, points | 11 to 12 | |
| 33 to 35 |
Alloy Composition
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.15 |
| Chromium (Cr), % | 0 | |
| 11.5 to 13.5 |
| Iron (Fe), % | 98.7 to 100 | |
| 81.8 to 87.3 |
| Manganese (Mn), % | 0 to 0.7 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 1.3 to 2.5 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.045 | |
| 0 to 0.030 |