EN 1.0034 Steel vs. AWS E309L

Both EN 1.0034 steel and AWS E309L are iron alloys. They have 61% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.0034 steel and the bottom bar is AWS E309L.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 9.0 to 32
34
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
79
Tensile Strength: Ultimate (UTS), MPa 340 to 380
580

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 53
15
Thermal Expansion, µm/m-K 12
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
20
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
3.7
Embodied Energy, MJ/kg 18
52
Embodied Water, L/kg 45
180

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 12 to 13
21
Strength to Weight: Bending, points 14 to 15
20
Thermal Diffusivity, mm2/s 14
4.0
Thermal Shock Resistance, points 11 to 12
15

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.040
Chromium (Cr), % 0
22 to 25
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 98.7 to 100
55.9 to 65.5
Manganese (Mn), % 0 to 0.7
0.5 to 2.5
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 0
12 to 14
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.045
0 to 0.030