EN 1.0034 Steel vs. C61500 Bronze
EN 1.0034 steel belongs to the iron alloys classification, while C61500 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.0034 steel and the bottom bar is C61500 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 9.0 to 32 | |
| 3.0 to 55 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 42 |
| Shear Strength, MPa | 220 to 230 | |
| 350 to 550 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 380 | |
| 480 to 970 |
| Tensile Strength: Yield (Proof), MPa | 180 to 280 | |
| 150 to 720 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 220 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1040 |
| Melting Onset (Solidus), °C | 1420 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 430 |
| Thermal Conductivity, W/m-K | 53 | |
| 58 |
| Thermal Expansion, µm/m-K | 12 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 13 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 29 |
| Density, g/cm3 | 7.9 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 3.2 |
| Embodied Energy, MJ/kg | 18 | |
| 52 |
| Embodied Water, L/kg | 45 | |
| 380 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 31 to 95 | |
| 27 to 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 84 to 210 | |
| 100 to 2310 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 12 to 13 | |
| 16 to 32 |
| Strength to Weight: Bending, points | 14 to 15 | |
| 16 to 26 |
| Thermal Diffusivity, mm2/s | 14 | |
| 16 |
| Thermal Shock Resistance, points | 11 to 12 | |
| 17 to 34 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 7.7 to 8.3 |
| Carbon (C), % | 0 to 0.15 | |
| 0 |
| Copper (Cu), % | 0 | |
| 89 to 90.5 |
| Iron (Fe), % | 98.7 to 100 | |
| 0 |
| Lead (Pb), % | 0 | |
| 0 to 0.015 |
| Manganese (Mn), % | 0 to 0.7 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 1.8 to 2.2 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 |
| Sulfur (S), % | 0 to 0.045 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |