EN 1.0308 Steel vs. EN 1.4518 Stainless Steel
Both EN 1.0308 steel and EN 1.4518 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.0308 steel and the bottom bar is EN 1.4518 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 7.8 to 28 | |
| 34 |
| Fatigue Strength, MPa | 140 to 200 | |
| 160 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 360 to 440 | |
| 490 |
| Tensile Strength: Yield (Proof), MPa | 190 to 340 | |
| 210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 300 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 1000 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1450 |
| Melting Onset (Solidus), °C | 1420 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 51 | |
| 15 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 2.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 2.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 20 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 4.0 |
| Embodied Energy, MJ/kg | 18 | |
| 55 |
| Embodied Water, L/kg | 46 | |
| 160 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 32 to 95 | |
| 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 93 to 300 | |
| 100 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 13 to 16 | |
| 17 |
| Strength to Weight: Bending, points | 14 to 16 | |
| 18 |
| Thermal Diffusivity, mm2/s | 14 | |
| 4.1 |
| Thermal Shock Resistance, points | 11 to 14 | |
| 14 |
Alloy Composition
| Carbon (C), % | 0 to 0.17 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 18 to 20 |
| Iron (Fe), % | 98.2 to 100 | |
| 61.4 to 70 |
| Manganese (Mn), % | 0 to 1.2 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 3.0 to 3.5 |
| Nickel (Ni), % | 0 | |
| 9.0 to 12 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 to 1.5 |
| Sulfur (S), % | 0 to 0.045 | |
| 0 to 0.030 |