EN 1.0308 Steel vs. Titanium 6-6-2
EN 1.0308 steel belongs to the iron alloys classification, while titanium 6-6-2 belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.0308 steel and the bottom bar is titanium 6-6-2.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 7.8 to 28 | |
| 6.7 to 9.0 |
| Fatigue Strength, MPa | 140 to 200 | |
| 590 to 670 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 73 | |
| 44 |
| Shear Strength, MPa | 230 to 260 | |
| 670 to 800 |
| Tensile Strength: Ultimate (UTS), MPa | 360 to 440 | |
| 1140 to 1370 |
| Tensile Strength: Yield (Proof), MPa | 190 to 340 | |
| 1040 to 1230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 310 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1610 |
| Melting Onset (Solidus), °C | 1420 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 540 |
| Thermal Conductivity, W/m-K | 51 | |
| 5.5 |
| Thermal Expansion, µm/m-K | 12 | |
| 9.4 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 1.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 2.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 40 |
| Density, g/cm3 | 7.9 | |
| 4.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 29 |
| Embodied Energy, MJ/kg | 18 | |
| 470 |
| Embodied Water, L/kg | 46 | |
| 200 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 32 to 95 | |
| 89 to 99 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 34 |
| Strength to Weight: Axial, points | 13 to 16 | |
| 66 to 79 |
| Strength to Weight: Bending, points | 14 to 16 | |
| 50 to 57 |
| Thermal Diffusivity, mm2/s | 14 | |
| 2.1 |
| Thermal Shock Resistance, points | 11 to 14 | |
| 75 to 90 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 5.0 to 6.0 |
| Carbon (C), % | 0 to 0.17 | |
| 0 to 0.050 |
| Copper (Cu), % | 0 | |
| 0.35 to 1.0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 98.2 to 100 | |
| 0.35 to 1.0 |
| Manganese (Mn), % | 0 to 1.2 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 5.0 to 6.0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.040 |
| Oxygen (O), % | 0 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 |
| Sulfur (S), % | 0 to 0.045 | |
| 0 |
| Tin (Sn), % | 0 | |
| 1.5 to 2.5 |
| Titanium (Ti), % | 0 | |
| 82.8 to 87.8 |
| Residuals, % | 0 | |
| 0 to 0.4 |