EN 1.0308 Steel vs. Z24311 Zinc

EN 1.0308 steel belongs to the iron alloys classification, while Z24311 zinc belongs to the zinc alloys. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0308 steel and the bottom bar is Z24311 zinc.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
87
Elongation at Break, % 7.8 to 28
63
Poisson's Ratio 0.29
0.25
Shear Modulus, GPa 73
35
Tensile Strength: Ultimate (UTS), MPa 360 to 440
140
Tensile Strength: Yield (Proof), MPa 190 to 340
120

Thermal Properties

Latent Heat of Fusion, J/g 250
110
Maximum Temperature: Mechanical, °C 400
90
Melting Completion (Liquidus), °C 1460
410
Melting Onset (Solidus), °C 1420
400
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 51
110
Thermal Expansion, µm/m-K 12
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
27
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
37

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
11
Density, g/cm3 7.9
6.6
Embodied Carbon, kg CO2/kg material 1.4
2.8
Embodied Energy, MJ/kg 18
53
Embodied Water, L/kg 46
340

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 32 to 95
85
Resilience: Unit (Modulus of Resilience), kJ/m3 93 to 300
81
Stiffness to Weight: Axial, points 13
7.4
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 13 to 16
6.1
Strength to Weight: Bending, points 14 to 16
9.3
Thermal Diffusivity, mm2/s 14
44
Thermal Shock Resistance, points 11 to 14
4.6

Alloy Composition

Aluminum (Al), % 0
0 to 0.0020
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.17
0
Copper (Cu), % 0
0 to 0.0050
Iron (Fe), % 98.2 to 100
0 to 0.010
Lead (Pb), % 0
0.030 to 0.080
Magnesium (Mg), % 0
0 to 0.0015
Manganese (Mn), % 0 to 1.2
0 to 0.015
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 0.35
0
Sulfur (S), % 0 to 0.045
0
Titanium (Ti), % 0
0 to 0.020
Zinc (Zn), % 0
99.862 to 100