EN 1.0314 Steel vs. ASTM Grade HG10 MNN Steel

Both EN 1.0314 steel and ASTM grade HG10 MNN steel are iron alloys. They have 63% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0314 steel and the bottom bar is ASTM grade HG10 MNN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 92 to 120
170
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 24 to 25
23
Fatigue Strength, MPa 140 to 220
170
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 320 to 400
590
Tensile Strength: Yield (Proof), MPa 190 to 310
250

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
990
Melting Completion (Liquidus), °C 1470
1420
Melting Onset (Solidus), °C 1430
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 53
15
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.9
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 7.9
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
21
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
4.0
Embodied Energy, MJ/kg 18
58
Embodied Water, L/kg 46
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 68 to 87
110
Resilience: Unit (Modulus of Resilience), kJ/m3 95 to 250
160
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 11 to 14
21
Strength to Weight: Bending, points 13 to 15
20
Thermal Diffusivity, mm2/s 14
3.9
Thermal Shock Resistance, points 10 to 13
13

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Carbon (C), % 0 to 0.030
0.070 to 0.11
Chromium (Cr), % 0
18.5 to 20.5
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 99.365 to 99.78
57.9 to 66.5
Manganese (Mn), % 0.2 to 0.4
3.0 to 5.0
Molybdenum (Mo), % 0
0.25 to 0.45
Nickel (Ni), % 0
11.5 to 13.5
Niobium (Nb), % 0
0.2 to 1.0
Nitrogen (N), % 0
0.2 to 0.3
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0 to 0.1
0 to 0.7
Sulfur (S), % 0 to 0.025
0 to 0.030