EN 1.0314 Steel vs. SAE-AISI H25 Steel

Both EN 1.0314 steel and SAE-AISI H25 steel are iron alloys. They have 80% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.0314 steel and the bottom bar is SAE-AISI H25 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
79
Tensile Strength: Ultimate (UTS), MPa 320 to 400
710 to 1620

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Melting Completion (Liquidus), °C 1470
1750
Melting Onset (Solidus), °C 1430
1700
Specific Heat Capacity, J/kg-K 470
420
Thermal Conductivity, W/m-K 53
26
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
38
Density, g/cm3 7.9
9.1
Embodied Carbon, kg CO2/kg material 1.4
6.2
Embodied Energy, MJ/kg 18
93
Embodied Water, L/kg 46
83

Common Calculations

Stiffness to Weight: Axial, points 13
12
Stiffness to Weight: Bending, points 24
22
Strength to Weight: Axial, points 11 to 14
22 to 50
Strength to Weight: Bending, points 13 to 15
20 to 34
Thermal Diffusivity, mm2/s 14
6.7
Thermal Shock Resistance, points 10 to 13
22 to 49

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0
Carbon (C), % 0 to 0.030
0.22 to 0.32
Chromium (Cr), % 0
3.8 to 4.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 99.365 to 99.78
77.2 to 81.3
Manganese (Mn), % 0.2 to 0.4
0.15 to 0.4
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0 to 0.1
0.15 to 0.4
Sulfur (S), % 0 to 0.025
0 to 0.030
Tungsten (W), % 0
14 to 16
Vanadium (V), % 0
0.4 to 0.6