EN 1.0314 Steel vs. C71520 Copper-nickel
EN 1.0314 steel belongs to the iron alloys classification, while C71520 copper-nickel belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.0314 steel and the bottom bar is C71520 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 140 |
| Elongation at Break, % | 24 to 25 | |
| 10 to 45 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 73 | |
| 51 |
| Shear Strength, MPa | 200 to 250 | |
| 250 to 340 |
| Tensile Strength: Ultimate (UTS), MPa | 320 to 400 | |
| 370 to 570 |
| Tensile Strength: Yield (Proof), MPa | 190 to 310 | |
| 140 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 260 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1170 |
| Melting Onset (Solidus), °C | 1430 | |
| 1120 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 400 |
| Thermal Conductivity, W/m-K | 53 | |
| 32 |
| Thermal Expansion, µm/m-K | 12 | |
| 15 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 6.9 | |
| 5.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.9 | |
| 5.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 40 |
| Density, g/cm3 | 7.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 5.0 |
| Embodied Energy, MJ/kg | 18 | |
| 73 |
| Embodied Water, L/kg | 46 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 68 to 87 | |
| 54 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 95 to 250 | |
| 67 to 680 |
| Stiffness to Weight: Axial, points | 13 | |
| 8.6 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 11 to 14 | |
| 12 to 18 |
| Strength to Weight: Bending, points | 13 to 15 | |
| 13 to 17 |
| Thermal Diffusivity, mm2/s | 14 | |
| 8.9 |
| Thermal Shock Resistance, points | 10 to 13 | |
| 12 to 19 |
Alloy Composition
| Aluminum (Al), % | 0.020 to 0.060 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.050 |
| Copper (Cu), % | 0 | |
| 65 to 71.6 |
| Iron (Fe), % | 99.365 to 99.78 | |
| 0.4 to 1.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0.2 to 0.4 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 | |
| 28 to 33 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.2 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.020 |
| Zinc (Zn), % | 0 | |
| 0 to 0.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |