EN 1.0314 Steel vs. N07041 Nickel
EN 1.0314 steel belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is EN 1.0314 steel and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Elongation at Break, % | 24 to 25 | |
| 14 |
| Fatigue Strength, MPa | 140 to 220 | |
| 540 |
| Shear Strength, MPa | 200 to 250 | |
| 850 |
| Tensile Strength: Ultimate (UTS), MPa | 320 to 400 | |
| 1400 |
| Tensile Strength: Yield (Proof), MPa | 190 to 310 | |
| 1050 |
Thermal Properties
| Melting Onset (Solidus), °C | 1430 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Conductivity, W/m-K | 53 | |
| 11 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.9 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 68 to 87 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 95 to 250 | |
| 2510 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 11 to 14 | |
| 47 |
| Strength to Weight: Bending, points | 13 to 15 | |
| 34 |
| Thermal Diffusivity, mm2/s | 14 | |
| 3.0 |
| Thermal Shock Resistance, points | 10 to 13 | |
| 38 |