EN 1.0478 Steel vs. Grey Cast Iron

Both EN 1.0478 steel and grey cast iron are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.0478 steel and the bottom bar is grey cast iron.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130
160 to 300
Elastic (Young's, Tensile) Modulus, GPa 190
180
Elongation at Break, % 24
9.6
Fatigue Strength, MPa 170
69 to 170
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
69
Shear Strength, MPa 280
180 to 610
Tensile Strength: Ultimate (UTS), MPa 440
160 to 450
Tensile Strength: Yield (Proof), MPa 230
98 to 290

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Melting Completion (Liquidus), °C 1460
1380
Melting Onset (Solidus), °C 1420
1180
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 49
46
Thermal Expansion, µm/m-K 12
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 2.2
1.9
Density, g/cm3 7.8
7.5
Embodied Carbon, kg CO2/kg material 1.5
1.5
Embodied Energy, MJ/kg 20
21
Embodied Water, L/kg 48
44

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90
13 to 37
Resilience: Unit (Modulus of Resilience), kJ/m3 150
27 to 240
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
5.8 to 17
Strength to Weight: Bending, points 16
8.7 to 17
Thermal Diffusivity, mm2/s 13
13
Thermal Shock Resistance, points 14
6.0 to 17

Alloy Composition

Aluminum (Al), % 0 to 0.060
0
Carbon (C), % 0 to 0.18
3.1 to 3.4
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.2
0
Iron (Fe), % 96.9 to 99.4
92.1 to 93.9
Manganese (Mn), % 0.6 to 1.4
0.5 to 0.7
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
0
Niobium (Nb), % 0 to 0.030
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0 to 0.9
Silicon (Si), % 0 to 0.4
2.5 to 2.8
Sulfur (S), % 0 to 0.015
0 to 0.15
Vanadium (V), % 0 to 0.050
0