EN 1.0590 Steel vs. AISI 316LN Stainless Steel

Both EN 1.0590 steel and AISI 316LN stainless steel are iron alloys. They have 68% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.0590 steel and the bottom bar is AISI 316LN stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
42
Fatigue Strength, MPa 290
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
82
Shear Strength, MPa 380
410
Tensile Strength: Ultimate (UTS), MPa 620
590
Tensile Strength: Yield (Proof), MPa 430
230

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
940
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
15
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
19
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.6
3.8
Embodied Energy, MJ/kg 22
53
Embodied Water, L/kg 48
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
200
Resilience: Unit (Modulus of Resilience), kJ/m3 480
130
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 14
4.1
Thermal Shock Resistance, points 20
13

Alloy Composition

Carbon (C), % 0 to 0.24
0 to 0.030
Chromium (Cr), % 0
16 to 18
Copper (Cu), % 0 to 0.6
0
Iron (Fe), % 96.4 to 100
62 to 71.9
Manganese (Mn), % 0 to 1.8
0 to 2.0
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 0
10 to 14
Niobium (Nb), % 0 to 0.060
0
Nitrogen (N), % 0 to 0.027
0.1 to 0.16
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 0.6
0 to 0.75
Sulfur (S), % 0 to 0.040
0 to 0.030
Titanium (Ti), % 0 to 0.060
0
Vanadium (V), % 0 to 0.15
0