EN 1.1147 Steel vs. EN 1.0314 Steel
Both EN 1.1147 steel and EN 1.0314 steel are iron alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is EN 1.1147 steel and the bottom bar is EN 1.0314 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 110 to 140 | |
| 92 to 120 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 12 to 17 | |
| 24 to 25 |
| Fatigue Strength, MPa | 180 to 250 | |
| 140 to 220 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 63 to 73 | |
| 78 to 86 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 280 | |
| 200 to 250 |
| Tensile Strength: Ultimate (UTS), MPa | 390 to 470 | |
| 320 to 400 |
| Tensile Strength: Yield (Proof), MPa | 280 to 370 | |
| 190 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1470 |
| Melting Onset (Solidus), °C | 1420 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 51 | |
| 53 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 6.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 7.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 18 | |
| 18 |
| Embodied Water, L/kg | 46 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 40 to 73 | |
| 68 to 87 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 to 370 | |
| 95 to 250 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 14 to 17 | |
| 11 to 14 |
| Strength to Weight: Bending, points | 15 to 17 | |
| 13 to 15 |
| Thermal Diffusivity, mm2/s | 14 | |
| 14 |
| Thermal Shock Resistance, points | 12 to 15 | |
| 10 to 13 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.020 to 0.060 |
| Carbon (C), % | 0.15 to 0.19 | |
| 0 to 0.030 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 98.3 to 99.25 | |
| 99.365 to 99.78 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0.2 to 0.4 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.025 |