EN 1.1170 Steel vs. EN 1.0308 Steel
Both EN 1.1170 steel and EN 1.0308 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is EN 1.1170 steel and the bottom bar is EN 1.0308 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 to 210 | |
| 100 to 130 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 16 to 17 | |
| 7.8 to 28 |
| Fatigue Strength, MPa | 220 to 330 | |
| 140 to 200 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 390 to 450 | |
| 230 to 260 |
| Tensile Strength: Ultimate (UTS), MPa | 640 to 730 | |
| 360 to 440 |
| Tensile Strength: Yield (Proof), MPa | 330 to 500 | |
| 190 to 340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 50 | |
| 51 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 8.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 1.4 |
| Embodied Energy, MJ/kg | 19 | |
| 18 |
| Embodied Water, L/kg | 49 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 91 to 100 | |
| 32 to 95 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 to 670 | |
| 93 to 300 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 23 to 26 | |
| 13 to 16 |
| Strength to Weight: Bending, points | 21 to 23 | |
| 14 to 16 |
| Thermal Diffusivity, mm2/s | 13 | |
| 14 |
| Thermal Shock Resistance, points | 20 to 23 | |
| 11 to 14 |
Alloy Composition
| Carbon (C), % | 0.25 to 0.32 | |
| 0 to 0.17 |
| Chromium (Cr), % | 0 to 0.4 | |
| 0 |
| Iron (Fe), % | 96.7 to 98.5 | |
| 98.2 to 100 |
| Manganese (Mn), % | 1.3 to 1.7 | |
| 0 to 1.2 |
| Molybdenum (Mo), % | 0 to 0.1 | |
| 0 |
| Nickel (Ni), % | 0 to 0.4 | |
| 0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.35 |
| Sulfur (S), % | 0 to 0.035 | |
| 0 to 0.045 |