EN 1.3542 Stainless Steel vs. AWS BVAg-29

EN 1.3542 stainless steel belongs to the iron alloys classification, while AWS BVAg-29 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is EN 1.3542 stainless steel and the bottom bar is AWS BVAg-29.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
73
Poisson's Ratio 0.28
0.37
Shear Modulus, GPa 76
27
Tensile Strength: Ultimate (UTS), MPa 720
180

Thermal Properties

Latent Heat of Fusion, J/g 270
120
Melting Completion (Liquidus), °C 1440
710
Melting Onset (Solidus), °C 1390
620
Specific Heat Capacity, J/kg-K 480
270
Thermal Expansion, µm/m-K 10
20

Otherwise Unclassified Properties

Density, g/cm3 7.7
9.7

Common Calculations

Stiffness to Weight: Axial, points 14
4.2
Stiffness to Weight: Bending, points 25
14
Strength to Weight: Axial, points 26
5.2
Strength to Weight: Bending, points 23
7.3
Thermal Shock Resistance, points 26
8.8

Alloy Composition

Cadmium (Cd), % 0
0 to 0.0010
Carbon (C), % 0.6 to 0.7
0 to 0.0050
Chromium (Cr), % 12.5 to 14.5
0
Copper (Cu), % 0
22.5 to 25.5
Indium (In), % 0
14 to 15
Iron (Fe), % 82.7 to 87.5
0
Lead (Pb), % 0
0 to 0.0020
Manganese (Mn), % 0 to 1.0
0
Molybdenum (Mo), % 0 to 0.75
0
Phosphorus (P), % 0 to 0.040
0 to 0.0020
Silicon (Si), % 0 to 1.0
0
Silver (Ag), % 0
60.5 to 62.5
Sulfur (S), % 0 to 0.030
0
Zinc (Zn), % 0
0 to 0.0010