EN 1.3555 Steel vs. Monel 400
EN 1.3555 steel belongs to the iron alloys classification, while Monel 400 belongs to the nickel alloys. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is EN 1.3555 steel and the bottom bar is Monel 400.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 160 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 75 | |
| 62 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 540 to 780 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 540 | |
| 1000 |
| Melting Completion (Liquidus), °C | 1500 | |
| 1350 |
| Melting Onset (Solidus), °C | 1450 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 430 |
| Thermal Expansion, µm/m-K | 13 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.3 | |
| 3.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 11 | |
| 3.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 50 |
| Density, g/cm3 | 7.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 5.6 | |
| 7.9 |
| Embodied Energy, MJ/kg | 81 | |
| 110 |
| Embodied Water, L/kg | 90 | |
| 250 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 10 |
| Stiffness to Weight: Bending, points | 24 | |
| 21 |
| Strength to Weight: Axial, points | 27 | |
| 17 to 25 |
| Strength to Weight: Bending, points | 23 | |
| 17 to 21 |
| Thermal Shock Resistance, points | 22 | |
| 17 to 25 |
Alloy Composition
| Carbon (C), % | 0.1 to 0.15 | |
| 0 to 0.3 |
| Chromium (Cr), % | 3.9 to 4.3 | |
| 0 |
| Copper (Cu), % | 0 to 0.1 | |
| 28 to 34 |
| Iron (Fe), % | 85.4 to 87.7 | |
| 0 to 2.5 |
| Manganese (Mn), % | 0.15 to 0.35 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 4.0 to 4.5 | |
| 0 |
| Nickel (Ni), % | 3.2 to 3.6 | |
| 63 to 72 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 |
| Silicon (Si), % | 0.1 to 0.25 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.024 |
| Tungsten (W), % | 0 to 0.15 | |
| 0 |
| Vanadium (V), % | 1.0 to 1.3 | |
| 0 |