EN 1.3555 Steel vs. SAE-AISI 9310 Steel
Both EN 1.3555 steel and SAE-AISI 9310 steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is EN 1.3555 steel and the bottom bar is SAE-AISI 9310 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 230 | |
540 to 610 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 75 | |
73 |
Tensile Strength: Ultimate (UTS), MPa | 770 | |
820 to 910 |
Thermal Properties
Latent Heat of Fusion, J/g | 260 | |
250 |
Maximum Temperature: Mechanical, °C | 540 | |
440 |
Melting Completion (Liquidus), °C | 1500 | |
1460 |
Melting Onset (Solidus), °C | 1450 | |
1420 |
Specific Heat Capacity, J/kg-K | 460 | |
470 |
Thermal Expansion, µm/m-K | 13 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 9.3 | |
7.7 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 11 | |
8.9 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 11 | |
4.4 |
Density, g/cm3 | 7.9 | |
7.9 |
Embodied Carbon, kg CO2/kg material | 5.6 | |
1.8 |
Embodied Energy, MJ/kg | 81 | |
24 |
Embodied Water, L/kg | 90 | |
57 |
Common Calculations
Stiffness to Weight: Axial, points | 14 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
24 |
Strength to Weight: Axial, points | 27 | |
29 to 32 |
Strength to Weight: Bending, points | 23 | |
25 to 27 |
Thermal Shock Resistance, points | 22 | |
24 to 27 |
Alloy Composition
Carbon (C), % | 0.1 to 0.15 | |
0.080 to 0.13 |
Chromium (Cr), % | 3.9 to 4.3 | |
1.0 to 1.4 |
Copper (Cu), % | 0 to 0.1 | |
0 |
Iron (Fe), % | 85.4 to 87.7 | |
93.8 to 95.2 |
Manganese (Mn), % | 0.15 to 0.35 | |
0.45 to 0.65 |
Molybdenum (Mo), % | 4.0 to 4.5 | |
0.080 to 0.15 |
Nickel (Ni), % | 3.2 to 3.6 | |
3.0 to 3.5 |
Phosphorus (P), % | 0 to 0.015 | |
0 to 0.015 |
Silicon (Si), % | 0.1 to 0.25 | |
0.2 to 0.35 |
Sulfur (S), % | 0 to 0.010 | |
0 to 0.012 |
Tungsten (W), % | 0 to 0.15 | |
0 |
Vanadium (V), % | 1.0 to 1.3 | |
0 |