EN 1.4020 Stainless Steel vs. SAE-AISI P2 Steel

Both EN 1.4020 stainless steel and SAE-AISI P2 steel are iron alloys. They have 69% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is EN 1.4020 stainless steel and the bottom bar is SAE-AISI P2 steel.

EN 1.4020 (X13CrMnNiN18-13-2) Stainless Steel SAE-AISI P2 (T51602) Low-Carbon Mould Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.28
Poisson's Ratio		0.29

Shear Modulus, GPa		77
Shear Modulus, GPa		73

Tensile Strength: Ultimate (UTS), MPa		770 to 1130
Tensile Strength: Ultimate (UTS), MPa		330 to 1980

Thermal Properties

Latent Heat of Fusion, J/g		280
Latent Heat of Fusion, J/g		250

Melting Completion (Liquidus), °C		1390
Melting Completion (Liquidus), °C		1460

Melting Onset (Solidus), °C		1350
Melting Onset (Solidus), °C		1420

Specific Heat Capacity, J/kg-K		480
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		17
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		11
Base Metal Price, % relative		2.7

Density, g/cm³		7.6
Density, g/cm³		7.9

Embodied Carbon, kg CO₂/kg material		2.5
Embodied Carbon, kg CO₂/kg material		1.5

Embodied Energy, MJ/kg		37
Embodied Energy, MJ/kg		20

Embodied Water, L/kg		150
Embodied Water, L/kg		51

Common Calculations

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		28 to 41
Strength to Weight: Axial, points		12 to 70

Strength to Weight: Bending, points		25 to 32
Strength to Weight: Bending, points		14 to 45

Thermal Shock Resistance, points		16 to 23
Thermal Shock Resistance, points		11 to 65

Alloy Composition

Carbon (C), %		0 to 0.15
Carbon (C), %		0 to 0.1

Chromium (Cr), %		16.5 to 19
Chromium (Cr), %		0.75 to 1.3

Copper (Cu), %		0
Copper (Cu), %		0 to 0.25

Iron (Fe), %		62.8 to 71.8
Iron (Fe), %		96.6 to 98.8

Manganese (Mn), %		11 to 14
Manganese (Mn), %		0.1 to 0.4

Molybdenum (Mo), %		0
Molybdenum (Mo), %		0.15 to 0.4

Nickel (Ni), %		0.5 to 2.5
Nickel (Ni), %		0.1 to 0.5

Nitrogen (N), %		0.2 to 0.45
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.045
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0.1 to 0.4

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030