EN 1.4028 Stainless Steel vs. EN 1.7362 Steel
Both EN 1.4028 stainless steel and EN 1.7362 steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.4028 stainless steel and the bottom bar is EN 1.7362 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 11 to 17 | |
| 21 to 22 |
| Fatigue Strength, MPa | 230 to 400 | |
| 140 to 250 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 74 |
| Shear Strength, MPa | 410 to 550 | |
| 320 to 370 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 930 | |
| 510 to 600 |
| Tensile Strength: Yield (Proof), MPa | 390 to 730 | |
| 200 to 360 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 760 | |
| 510 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1460 |
| Melting Onset (Solidus), °C | 1400 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 30 | |
| 40 |
| Thermal Expansion, µm/m-K | 11 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.8 | |
| 8.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.2 | |
| 9.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 7.0 | |
| 4.5 |
| Density, g/cm3 | 7.7 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 1.8 |
| Embodied Energy, MJ/kg | 27 | |
| 23 |
| Embodied Water, L/kg | 100 | |
| 69 |
Common Calculations
| PREN (Pitting Resistance) | 13 | |
| 6.9 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 94 to 96 | |
| 90 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 380 to 1360 | |
| 100 to 340 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 24 to 33 | |
| 18 to 21 |
| Strength to Weight: Bending, points | 22 to 27 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 8.1 | |
| 11 |
| Thermal Shock Resistance, points | 23 to 32 | |
| 14 to 17 |
Alloy Composition
| Carbon (C), % | 0.26 to 0.35 | |
| 0.1 to 0.15 |
| Chromium (Cr), % | 12 to 14 | |
| 4.0 to 6.0 |
| Copper (Cu), % | 0 | |
| 0 to 0.3 |
| Iron (Fe), % | 83.1 to 87.7 | |
| 91.5 to 95.2 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0.3 to 0.6 |
| Molybdenum (Mo), % | 0 | |
| 0.45 to 0.65 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Nitrogen (N), % | 0 | |
| 0 to 0.012 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.0050 |