EN 1.4028 (X30Cr13) Stainless Steel
EN 1.4028 stainless steel is a martensitic stainless steel formulated for primary forming into wrought products. 1.4028 is the EN numeric designation for this material. X30Cr13 is the EN chemical designation.
It has a moderately low embodied energy among the wrought martensitic stainless steels in the database.
The properties of EN 1.4028 stainless steel include three common variations. This page shows summary ranges across all of them. For more specific values, follow the links immediately below. The graph bars on the material properties cards further below compare EN 1.4028 stainless steel to: wrought martensitic stainless steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
190 GPa 28 x 106 psi
Elongation at Break
11 to 17 %
Fatigue Strength
230 to 400 MPa 34 to 58 x 103 psi
Poisson's Ratio
0.28
Shear Modulus
76 GPa 11 x 106 psi
Shear Strength
410 to 550 MPa 59 to 80 x 103 psi
Tensile Strength: Ultimate (UTS)
660 to 930 MPa 96 to 130 x 103 psi
Tensile Strength: Yield (Proof)
390 to 730 MPa 56 to 110 x 103 psi
Thermal Properties
Latent Heat of Fusion
270 J/g
Maximum Temperature: Corrosion
390 °C 730 °F
Maximum Temperature: Mechanical
760 °C 1390 °F
Melting Completion (Liquidus)
1440 °C 2620 °F
Melting Onset (Solidus)
1400 °C 2550 °F
Specific Heat Capacity
480 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
30 W/m-K 17 BTU/h-ft-°F
Thermal Expansion
11 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
2.8 % IACS
Electrical Conductivity: Equal Weight (Specific)
3.2 % IACS
Otherwise Unclassified Properties
Base Metal Price
7.0 % relative
Density
7.7 g/cm3 480 lb/ft3
Embodied Carbon
1.9 kg CO2/kg material
Embodied Energy
27 MJ/kg 12 x 103 BTU/lb
Embodied Water
100 L/kg 12 gal/lb
Common Calculations
PREN (Pitting Resistance)
13
Resilience: Ultimate (Unit Rupture Work)
94 to 96 MJ/m3
Resilience: Unit (Modulus of Resilience)
380 to 1360 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
25 points
Strength to Weight: Axial
24 to 33 points
Strength to Weight: Bending
22 to 27 points
Thermal Diffusivity
8.1 mm2/s
Thermal Shock Resistance
23 to 32 points
Alloy Composition
Among wrought stainless steels, the composition of EN 1.4028 stainless steel is notable for containing comparatively high amounts of chromium (Cr) and manganese (Mn). Chromium is the defining alloying element of stainless steel. Higher chromium content imparts additional corrosion resistance. Manganese is used to improve ductility at elevated temperatures. It also permits a higher nitrogen content than would otherwise be possible.
| Fe | 83.1 to 87.7 | |
| Cr | 12 to 14 | |
| Mn | 0 to 1.5 | |
| Si | 0 to 1.0 | |
| C | 0.26 to 0.35 | |
| P | 0 to 0.040 | |
| S | 0 to 0.015 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Similar Alloys
Further Reading
EN 10250-4: Open die steel forgings for general engineering purposes - Part 4: Stainless steels
EN 10088-2: Stainless steels - Part 2: Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes
Machining of Stainless Steels and Super Alloys: Traditional and Nontraditional Techniques, Helmi A. Youssef, 2016
EN 10088-3: Stainless steels - Part 3: Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes
EN 10088-1: Stainless steels - Part 1: List of stainless steels
Corrosion of Stainless Steels, A. John Sedriks, 1996
Advances in Stainless Steels, Baldev Raj et al. (editors), 2010