EN 1.4028 Stainless Steel vs. N07041 Nickel
EN 1.4028 stainless steel belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is EN 1.4028 stainless steel and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
220 |
Elongation at Break, % | 11 to 17 | |
14 |
Fatigue Strength, MPa | 230 to 400 | |
540 |
Shear Strength, MPa | 410 to 550 | |
850 |
Tensile Strength: Ultimate (UTS), MPa | 660 to 930 | |
1400 |
Tensile Strength: Yield (Proof), MPa | 390 to 730 | |
1050 |
Thermal Properties
Melting Onset (Solidus), °C | 1400 | |
1320 |
Specific Heat Capacity, J/kg-K | 480 | |
450 |
Thermal Conductivity, W/m-K | 30 | |
11 |
Thermal Expansion, µm/m-K | 11 | |
12 |
Otherwise Unclassified Properties
Density, g/cm3 | 7.7 | |
8.2 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 94 to 96 | |
180 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 380 to 1360 | |
2510 |
Stiffness to Weight: Axial, points | 14 | |
15 |
Stiffness to Weight: Bending, points | 25 | |
25 |
Strength to Weight: Axial, points | 24 to 33 | |
47 |
Strength to Weight: Bending, points | 22 to 27 | |
34 |
Thermal Diffusivity, mm2/s | 8.1 | |
3.0 |
Thermal Shock Resistance, points | 23 to 32 | |
38 |