EN 1.4035 Stainless Steel vs. N08332 Stainless Steel

Both EN 1.4035 stainless steel and N08332 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 58% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4035 stainless steel and the bottom bar is N08332 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
170
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 18
34
Fatigue Strength, MPa 250
170
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Shear Strength, MPa 430
350
Tensile Strength: Ultimate (UTS), MPa 690
520
Tensile Strength: Yield (Proof), MPa 400
210

Thermal Properties

Latent Heat of Fusion, J/g 270
310
Maximum Temperature: Corrosion, °C 380
420
Maximum Temperature: Mechanical, °C 760
1050
Melting Completion (Liquidus), °C 1430
1390
Melting Onset (Solidus), °C 1390
1340
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 29
12
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.0
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 3.5
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
32
Density, g/cm3 7.7
8.0
Embodied Carbon, kg CO2/kg material 2.0
5.4
Embodied Energy, MJ/kg 27
77
Embodied Water, L/kg 100
190

Common Calculations

PREN (Pitting Resistance) 13
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
140
Resilience: Unit (Modulus of Resilience), kJ/m3 420
110
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 25
18
Strength to Weight: Bending, points 22
18
Thermal Diffusivity, mm2/s 7.8
3.1
Thermal Shock Resistance, points 25
12

Alloy Composition

Carbon (C), % 0.43 to 0.5
0.050 to 0.1
Chromium (Cr), % 12.5 to 14
17 to 20
Copper (Cu), % 0
0 to 1.0
Iron (Fe), % 82.1 to 86.9
38.3 to 48.2
Lead (Pb), % 0
0 to 0.0050
Manganese (Mn), % 0 to 2.0
0 to 2.0
Nickel (Ni), % 0
34 to 37
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0.75 to 1.5
Sulfur (S), % 0.15 to 0.35
0 to 0.030
Tin (Sn), % 0
0 to 0.025