EN 1.4301 Stainless Steel vs. CC765S Brass

EN 1.4301 stainless steel belongs to the iron alloys classification, while CC765S brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4301 stainless steel and the bottom bar is CC765S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190 to 270
130
Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 14 to 46
21
Poisson's Ratio 0.28
0.31
Shear Modulus, GPa 77
42
Tensile Strength: Ultimate (UTS), MPa 610 to 900
540
Tensile Strength: Yield (Proof), MPa 220 to 570
220

Thermal Properties

Latent Heat of Fusion, J/g 290
180
Maximum Temperature: Mechanical, °C 940
140
Melting Completion (Liquidus), °C 1430
860
Melting Onset (Solidus), °C 1380
820
Specific Heat Capacity, J/kg-K 480
400
Thermal Conductivity, W/m-K 15
91
Thermal Expansion, µm/m-K 16
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
30
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
34

Otherwise Unclassified Properties

Base Metal Price, % relative 15
24
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 3.0
3.0
Embodied Energy, MJ/kg 43
51
Embodied Water, L/kg 140
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 220
90
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 820
220
Stiffness to Weight: Axial, points 14
7.6
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 22 to 32
19
Strength to Weight: Bending, points 20 to 27
18
Thermal Diffusivity, mm2/s 4.0
28
Thermal Shock Resistance, points 14 to 20
17

Alloy Composition

Aluminum (Al), % 0
0.5 to 2.5
Antimony (Sb), % 0
0 to 0.080
Carbon (C), % 0 to 0.070
0
Chromium (Cr), % 17.5 to 19.5
0
Copper (Cu), % 0
51 to 65
Iron (Fe), % 66.8 to 74.5
0.5 to 2.0
Lead (Pb), % 0
0 to 0.5
Manganese (Mn), % 0 to 2.0
0.3 to 3.0
Nickel (Ni), % 8.0 to 10.5
0 to 6.0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.1
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 1.0
Zinc (Zn), % 0
19.8 to 47.7