EN 1.4305 Stainless Steel vs. EN 1.0453 Steel

Both EN 1.4305 stainless steel and EN 1.0453 steel are iron alloys. They have 72% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4305 stainless steel and the bottom bar is EN 1.0453 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 270
140
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 14 to 40
26
Fatigue Strength, MPa 190 to 330
220
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 420 to 550
320
Tensile Strength: Ultimate (UTS), MPa 610 to 900
490
Tensile Strength: Yield (Proof), MPa 220 to 570
300

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 930
400
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
49
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 15
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.0
1.5
Embodied Energy, MJ/kg 42
20
Embodied Water, L/kg 140
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 190
110
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 830
230
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22 to 32
17
Strength to Weight: Bending, points 20 to 27
18
Thermal Diffusivity, mm2/s 4.0
13
Thermal Shock Resistance, points 14 to 20
15

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Carbon (C), % 0 to 0.1
0 to 0.2
Chromium (Cr), % 17 to 19
0 to 0.3
Copper (Cu), % 0 to 1.0
0 to 0.3
Iron (Fe), % 66.4 to 74.9
96.9 to 99.38
Manganese (Mn), % 0 to 2.0
0.6 to 1.4
Molybdenum (Mo), % 0
0 to 0.080
Nickel (Ni), % 8.0 to 10
0 to 0.3
Niobium (Nb), % 0
0 to 0.010
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0.15 to 0.35
0 to 0.010
Titanium (Ti), % 0
0 to 0.040
Vanadium (V), % 0
0 to 0.020