EN 1.4305 Stainless Steel vs. C61000 Bronze

EN 1.4305 stainless steel belongs to the iron alloys classification, while C61000 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4305 stainless steel and the bottom bar is C61000 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 14 to 40
29 to 50
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 77
42
Shear Strength, MPa 420 to 550
280 to 300
Tensile Strength: Ultimate (UTS), MPa 610 to 900
390 to 460
Tensile Strength: Yield (Proof), MPa 220 to 570
150 to 190

Thermal Properties

Latent Heat of Fusion, J/g 290
220
Maximum Temperature: Mechanical, °C 930
210
Melting Completion (Liquidus), °C 1420
1040
Melting Onset (Solidus), °C 1380
990
Specific Heat Capacity, J/kg-K 480
420
Thermal Conductivity, W/m-K 15
69
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
15
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
16

Otherwise Unclassified Properties

Base Metal Price, % relative 15
29
Density, g/cm3 7.8
8.5
Embodied Carbon, kg CO2/kg material 3.0
3.0
Embodied Energy, MJ/kg 42
49
Embodied Water, L/kg 140
370

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 190
110 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 120 to 830
100 to 160
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 22 to 32
13 to 15
Strength to Weight: Bending, points 20 to 27
14 to 16
Thermal Diffusivity, mm2/s 4.0
19
Thermal Shock Resistance, points 14 to 20
14 to 16

Alloy Composition

Aluminum (Al), % 0
6.0 to 8.5
Carbon (C), % 0 to 0.1
0
Chromium (Cr), % 17 to 19
0
Copper (Cu), % 0 to 1.0
90.2 to 94
Iron (Fe), % 66.4 to 74.9
0 to 0.5
Lead (Pb), % 0
0 to 0.020
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 8.0 to 10
0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.0
0 to 0.1
Sulfur (S), % 0.15 to 0.35
0
Zinc (Zn), % 0
0 to 0.2
Residuals, % 0
0 to 0.5

Comparable Variants