EN 1.4305 Stainless Steel vs. N06002 Nickel
EN 1.4305 stainless steel belongs to the iron alloys classification, while N06002 nickel belongs to the nickel alloys. They have 47% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.4305 stainless steel and the bottom bar is N06002 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 210 |
| Elongation at Break, % | 14 to 40 | |
| 41 |
| Fatigue Strength, MPa | 190 to 330 | |
| 250 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 81 |
| Shear Strength, MPa | 420 to 550 | |
| 520 |
| Tensile Strength: Ultimate (UTS), MPa | 610 to 900 | |
| 760 |
| Tensile Strength: Yield (Proof), MPa | 220 to 570 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 930 | |
| 990 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1360 |
| Melting Onset (Solidus), °C | 1380 | |
| 1260 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 450 |
| Thermal Conductivity, W/m-K | 15 | |
| 9.9 |
| Thermal Expansion, µm/m-K | 16 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 1.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 55 |
| Density, g/cm3 | 7.8 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 9.3 |
| Embodied Energy, MJ/kg | 42 | |
| 130 |
| Embodied Water, L/kg | 140 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 190 | |
| 250 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 to 830 | |
| 230 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 22 to 32 | |
| 25 |
| Strength to Weight: Bending, points | 20 to 27 | |
| 22 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 2.6 |
| Thermal Shock Resistance, points | 14 to 20 | |
| 19 |
Alloy Composition
| Carbon (C), % | 0 to 0.1 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 17 to 19 | |
| 20.5 to 23 |
| Cobalt (Co), % | 0 | |
| 0.5 to 2.5 |
| Copper (Cu), % | 0 to 1.0 | |
| 0 |
| Iron (Fe), % | 66.4 to 74.9 | |
| 17 to 20 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 8.0 to 10 |
| Nickel (Ni), % | 8.0 to 10 | |
| 42.3 to 54 |
| Nitrogen (N), % | 0 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0.15 to 0.35 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 0.2 to 1.0 |