EN 1.4311 Stainless Steel vs. ASTM A372 Grade K Steel

Both EN 1.4311 stainless steel and ASTM A372 grade K steel are iron alloys. They have 74% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4311 stainless steel and the bottom bar is ASTM A372 grade K steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
230
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 43
23
Fatigue Strength, MPa 270
440
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 450
490
Tensile Strength: Ultimate (UTS), MPa 650
780
Tensile Strength: Yield (Proof), MPa 310
620

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 950
440
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
48
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 16
4.4
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.1
1.8
Embodied Energy, MJ/kg 43
24
Embodied Water, L/kg 140
57

Common Calculations

PREN (Pitting Resistance) 21
2.7
Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
160
Resilience: Unit (Modulus of Resilience), kJ/m3 240
1010
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
27
Strength to Weight: Bending, points 21
24
Thermal Diffusivity, mm2/s 4.0
13
Thermal Shock Resistance, points 15
23

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.18
Chromium (Cr), % 17.5 to 19.5
1.0 to 1.8
Iron (Fe), % 65.7 to 73.9
93.4 to 96.6
Manganese (Mn), % 0 to 2.0
0.1 to 0.4
Molybdenum (Mo), % 0
0.2 to 0.6
Nickel (Ni), % 8.5 to 11.5
2.0 to 3.3
Nitrogen (N), % 0.12 to 0.22
0
Phosphorus (P), % 0 to 0.045
0 to 0.015
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.015
0 to 0.010