EN 1.4311 Stainless Steel vs. EN 1.4919 Stainless Steel

Both EN 1.4311 stainless steel and EN 1.4919 stainless steel are iron alloys. Both are furnished in the solution annealed (AT) condition. They have a very high 96% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.4311 stainless steel and the bottom bar is EN 1.4919 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
180
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 43
40
Fatigue Strength, MPa 270
200
Impact Strength: V-Notched Charpy, J 93
110
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
78
Shear Strength, MPa 450
400
Tensile Strength: Ultimate (UTS), MPa 650
590
Tensile Strength: Yield (Proof), MPa 310
230

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Maximum Temperature: Corrosion, °C 420
410
Maximum Temperature: Mechanical, °C 950
950
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
16
Thermal Expansion, µm/m-K 16
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 16
19
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.1
3.8
Embodied Energy, MJ/kg 43
52
Embodied Water, L/kg 140
150

Common Calculations

PREN (Pitting Resistance) 21
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
190
Resilience: Unit (Modulus of Resilience), kJ/m3 240
130
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 23
21
Strength to Weight: Bending, points 21
20
Thermal Diffusivity, mm2/s 4.0
4.3
Thermal Shock Resistance, points 15
13

Alloy Composition

Boron (B), % 0
0.0015 to 0.0050
Carbon (C), % 0 to 0.030
0.040 to 0.080
Chromium (Cr), % 17.5 to 19.5
16.5 to 18.5
Iron (Fe), % 65.7 to 73.9
62.8 to 71.5
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 0
2.0 to 2.5
Nickel (Ni), % 8.5 to 11.5
10 to 13
Nitrogen (N), % 0.12 to 0.22
0 to 0.1
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015