EN 1.4311 Stainless Steel vs. C43000 Brass

EN 1.4311 stainless steel belongs to the iron alloys classification, while C43000 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4311 stainless steel and the bottom bar is C43000 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 43
3.0 to 55
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 77
42
Shear Strength, MPa 450
230 to 410
Tensile Strength: Ultimate (UTS), MPa 650
320 to 710
Tensile Strength: Yield (Proof), MPa 310
130 to 550

Thermal Properties

Latent Heat of Fusion, J/g 290
190
Maximum Temperature: Mechanical, °C 950
170
Melting Completion (Liquidus), °C 1420
1030
Melting Onset (Solidus), °C 1380
1000
Specific Heat Capacity, J/kg-K 480
380
Thermal Conductivity, W/m-K 15
120
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
27
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
28

Otherwise Unclassified Properties

Base Metal Price, % relative 16
29
Density, g/cm3 7.8
8.6
Embodied Carbon, kg CO2/kg material 3.1
2.8
Embodied Energy, MJ/kg 43
46
Embodied Water, L/kg 140
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
20 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 240
82 to 1350
Stiffness to Weight: Axial, points 14
7.1
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 23
10 to 23
Strength to Weight: Bending, points 21
12 to 20
Thermal Diffusivity, mm2/s 4.0
36
Thermal Shock Resistance, points 15
11 to 25

Alloy Composition

Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 17.5 to 19.5
0
Copper (Cu), % 0
84 to 87
Iron (Fe), % 65.7 to 73.9
0 to 0.050
Lead (Pb), % 0
0 to 0.1
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 8.5 to 11.5
0
Nitrogen (N), % 0.12 to 0.22
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
1.7 to 2.7
Zinc (Zn), % 0
9.7 to 14.3
Residuals, % 0
0 to 0.5