EN 1.4317 Stainless Steel vs. N08332 Stainless Steel

Both EN 1.4317 stainless steel and N08332 stainless steel are iron alloys. They have 61% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4317 stainless steel and the bottom bar is N08332 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 17
34
Fatigue Strength, MPa 380
170
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Tensile Strength: Ultimate (UTS), MPa 860
520
Tensile Strength: Yield (Proof), MPa 630
210

Thermal Properties

Latent Heat of Fusion, J/g 280
310
Maximum Temperature: Corrosion, °C 390
420
Maximum Temperature: Mechanical, °C 770
1050
Melting Completion (Liquidus), °C 1440
1390
Melting Onset (Solidus), °C 1400
1340
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 26
12
Thermal Expansion, µm/m-K 11
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.7
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 3.2
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 10
32
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 2.4
5.4
Embodied Energy, MJ/kg 33
77
Embodied Water, L/kg 110
190

Common Calculations

PREN (Pitting Resistance) 14
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
140
Resilience: Unit (Modulus of Resilience), kJ/m3 1010
110
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 31
18
Strength to Weight: Bending, points 26
18
Thermal Diffusivity, mm2/s 7.0
3.1
Thermal Shock Resistance, points 30
12

Alloy Composition

Carbon (C), % 0 to 0.060
0.050 to 0.1
Chromium (Cr), % 12 to 13.5
17 to 20
Copper (Cu), % 0
0 to 1.0
Iron (Fe), % 78.7 to 84.5
38.3 to 48.2
Lead (Pb), % 0
0 to 0.0050
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0 to 0.7
0
Nickel (Ni), % 3.5 to 5.0
34 to 37
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 1.0
0.75 to 1.5
Sulfur (S), % 0 to 0.025
0 to 0.030
Tin (Sn), % 0
0 to 0.025