EN 1.4401 Stainless Steel vs. Monel 400
EN 1.4401 stainless steel belongs to the iron alloys classification, while Monel 400 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.4401 stainless steel and the bottom bar is Monel 400.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 160 |
| Elongation at Break, % | 14 to 40 | |
| 20 to 40 |
| Fatigue Strength, MPa | 200 to 320 | |
| 230 to 290 |
| Poisson's Ratio | 0.28 | |
| 0.32 |
| Shear Modulus, GPa | 78 | |
| 62 |
| Shear Strength, MPa | 410 to 550 | |
| 370 to 490 |
| Tensile Strength: Ultimate (UTS), MPa | 600 to 900 | |
| 540 to 780 |
| Tensile Strength: Yield (Proof), MPa | 230 to 570 | |
| 210 to 590 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 950 | |
| 1000 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1350 |
| Melting Onset (Solidus), °C | 1400 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 430 |
| Thermal Conductivity, W/m-K | 15 | |
| 23 |
| Thermal Expansion, µm/m-K | 16 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 3.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 3.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 19 | |
| 50 |
| Density, g/cm3 | 7.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 3.8 | |
| 7.9 |
| Embodied Energy, MJ/kg | 52 | |
| 110 |
| Embodied Water, L/kg | 150 | |
| 250 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 190 | |
| 140 to 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 800 | |
| 140 to 1080 |
| Stiffness to Weight: Axial, points | 14 | |
| 10 |
| Stiffness to Weight: Bending, points | 25 | |
| 21 |
| Strength to Weight: Axial, points | 21 to 32 | |
| 17 to 25 |
| Strength to Weight: Bending, points | 20 to 26 | |
| 17 to 21 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 6.1 |
| Thermal Shock Resistance, points | 13 to 20 | |
| 17 to 25 |
Alloy Composition
| Carbon (C), % | 0 to 0.070 | |
| 0 to 0.3 |
| Chromium (Cr), % | 16.5 to 18.5 | |
| 0 |
| Copper (Cu), % | 0 | |
| 28 to 34 |
| Iron (Fe), % | 62.8 to 71.5 | |
| 0 to 2.5 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 2.0 to 2.5 | |
| 0 |
| Nickel (Ni), % | 10 to 13 | |
| 63 to 72 |
| Nitrogen (N), % | 0 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.024 |