EN 1.4408 Stainless Steel vs. EN 1.4110 Stainless Steel

Both EN 1.4408 stainless steel and EN 1.4110 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4408 stainless steel and the bottom bar is EN 1.4110 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
11 to 14
Fatigue Strength, MPa 170
250 to 730
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
76
Tensile Strength: Ultimate (UTS), MPa 510
770 to 1720
Tensile Strength: Yield (Proof), MPa 210
430 to 1330

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 420
390
Maximum Temperature: Mechanical, °C 990
790
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1390
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
30
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 18
8.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.7
2.3
Embodied Energy, MJ/kg 52
33
Embodied Water, L/kg 150
110

Common Calculations

PREN (Pitting Resistance) 26
16
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
90 to 180
Resilience: Unit (Modulus of Resilience), kJ/m3 110
480 to 4550
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 18
28 to 62
Strength to Weight: Bending, points 18
24 to 41
Thermal Diffusivity, mm2/s 3.9
8.1
Thermal Shock Resistance, points 11
27 to 60

Alloy Composition

Carbon (C), % 0 to 0.070
0.48 to 0.6
Chromium (Cr), % 18 to 20
13 to 15
Iron (Fe), % 62.4 to 71
81.4 to 86
Manganese (Mn), % 0 to 1.5
0 to 1.0
Molybdenum (Mo), % 2.0 to 2.5
0.5 to 0.8
Nickel (Ni), % 9.0 to 12
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Vanadium (V), % 0
0 to 0.15