EN 1.4408 Stainless Steel vs. EN 1.7767 Steel

Both EN 1.4408 stainless steel and EN 1.7767 steel are iron alloys. They have 71% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4408 stainless steel and the bottom bar is EN 1.7767 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
200 to 210
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
20
Fatigue Strength, MPa 170
320 to 340
Impact Strength: V-Notched Charpy, J 67
46
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
74
Tensile Strength: Ultimate (UTS), MPa 510
670 to 690
Tensile Strength: Yield (Proof), MPa 210
460 to 500

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 990
480
Melting Completion (Liquidus), °C 1440
1470
Melting Onset (Solidus), °C 1390
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
40
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 18
4.5
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.7
2.4
Embodied Energy, MJ/kg 52
33
Embodied Water, L/kg 150
64

Common Calculations

PREN (Pitting Resistance) 26
6.4
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
120 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 110
570 to 650
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
24
Strength to Weight: Bending, points 18
22
Thermal Diffusivity, mm2/s 3.9
11
Thermal Shock Resistance, points 11
19 to 20

Alloy Composition

Carbon (C), % 0 to 0.070
0.1 to 0.15
Chromium (Cr), % 18 to 20
2.8 to 3.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 62.4 to 71
93.8 to 95.8
Manganese (Mn), % 0 to 1.5
0.3 to 0.6
Molybdenum (Mo), % 2.0 to 2.5
0.9 to 1.1
Nickel (Ni), % 9.0 to 12
0 to 0.25
Niobium (Nb), % 0
0 to 0.070
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.040
0 to 0.015
Silicon (Si), % 0 to 1.5
0 to 0.15
Sulfur (S), % 0 to 0.030
0 to 0.0050
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0.2 to 0.3