EN 1.4408 Stainless Steel vs. CC767S Brass

EN 1.4408 stainless steel belongs to the iron alloys classification, while CC767S brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4408 stainless steel and the bottom bar is CC767S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
86
Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 34
34
Poisson's Ratio 0.28
0.31
Shear Modulus, GPa 78
40
Tensile Strength: Ultimate (UTS), MPa 510
430
Tensile Strength: Yield (Proof), MPa 210
150

Thermal Properties

Latent Heat of Fusion, J/g 300
180
Maximum Temperature: Mechanical, °C 990
120
Melting Completion (Liquidus), °C 1440
840
Melting Onset (Solidus), °C 1390
790
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 15
110
Thermal Expansion, µm/m-K 16
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
32
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
36

Otherwise Unclassified Properties

Base Metal Price, % relative 18
23
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 3.7
2.7
Embodied Energy, MJ/kg 52
47
Embodied Water, L/kg 150
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
110
Resilience: Unit (Modulus of Resilience), kJ/m3 110
100
Stiffness to Weight: Axial, points 14
7.3
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 18
15
Strength to Weight: Bending, points 18
16
Thermal Diffusivity, mm2/s 3.9
34
Thermal Shock Resistance, points 11
14

Alloy Composition

Aluminum (Al), % 0
0.1 to 0.8
Carbon (C), % 0 to 0.070
0
Chromium (Cr), % 18 to 20
0
Copper (Cu), % 0
58 to 64
Iron (Fe), % 62.4 to 71
0 to 0.5
Lead (Pb), % 0
0 to 0.1
Manganese (Mn), % 0 to 1.5
0 to 0.5
Molybdenum (Mo), % 2.0 to 2.5
0
Nickel (Ni), % 9.0 to 12
0 to 1.0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.5
0 to 0.2
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0 to 0.1
Zinc (Zn), % 0
32.8 to 41.9