EN 1.4470 Stainless Steel vs. AISI 316Cb Stainless Steel

Both EN 1.4470 stainless steel and AISI 316Cb stainless steel are iron alloys. They have a moderately high 93% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4470 stainless steel and the bottom bar is AISI 316Cb stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 23
34
Fatigue Strength, MPa 320
180
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
78
Tensile Strength: Ultimate (UTS), MPa 680
580
Tensile Strength: Yield (Proof), MPa 480
230

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 430
490
Maximum Temperature: Mechanical, °C 1060
940
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 18
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 17
22
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.6
4.4
Embodied Energy, MJ/kg 49
61
Embodied Water, L/kg 160
150

Common Calculations

PREN (Pitting Resistance) 34
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
160
Resilience: Unit (Modulus of Resilience), kJ/m3 570
130
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 24
20
Strength to Weight: Bending, points 22
20
Thermal Diffusivity, mm2/s 4.8
4.1
Thermal Shock Resistance, points 18
13

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 21 to 23
16 to 18
Iron (Fe), % 63.7 to 71.9
60.9 to 72
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 2.5 to 3.5
2.0 to 3.0
Nickel (Ni), % 4.5 to 6.5
10 to 14
Niobium (Nb), % 0
0 to 1.1
Nitrogen (N), % 0.12 to 0.2
0 to 0.1
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.025
0 to 0.030