EN 1.4470 Stainless Steel vs. EN 1.4948 Stainless Steel

Both EN 1.4470 stainless steel and EN 1.4948 stainless steel are iron alloys. Both are furnished in the solution annealed (AT) condition. They have a moderately high 93% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4470 stainless steel and the bottom bar is EN 1.4948 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 23
48
Fatigue Strength, MPa 320
200
Impact Strength: V-Notched Charpy, J 34
100
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
77
Tensile Strength: Ultimate (UTS), MPa 680
610
Tensile Strength: Yield (Proof), MPa 480
210

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Maximum Temperature: Corrosion, °C 430
410
Maximum Temperature: Mechanical, °C 1060
930
Melting Completion (Liquidus), °C 1450
1430
Melting Onset (Solidus), °C 1400
1380
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 18
17
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 17
15
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.6
3.0
Embodied Energy, MJ/kg 49
43
Embodied Water, L/kg 160
140

Common Calculations

PREN (Pitting Resistance) 34
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
230
Resilience: Unit (Modulus of Resilience), kJ/m3 570
110
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 24
22
Strength to Weight: Bending, points 22
21
Thermal Diffusivity, mm2/s 4.8
4.5
Thermal Shock Resistance, points 18
14

Alloy Composition

Carbon (C), % 0 to 0.030
0.040 to 0.080
Chromium (Cr), % 21 to 23
17 to 19
Iron (Fe), % 63.7 to 71.9
66.8 to 75
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 2.5 to 3.5
0
Nickel (Ni), % 4.5 to 6.5
8.0 to 11
Nitrogen (N), % 0.12 to 0.2
0 to 0.1
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015