EN 1.4490 Stainless Steel vs. N07716 Nickel
EN 1.4490 stainless steel belongs to the iron alloys classification, while N07716 nickel belongs to the nickel alloys. They have a modest 38% of their average alloy composition in common, which, by itself, doesn't mean much. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.4490 stainless steel and the bottom bar is N07716 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 34 | |
| 34 |
| Fatigue Strength, MPa | 210 | |
| 690 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 78 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 560 | |
| 860 |
| Tensile Strength: Yield (Proof), MPa | 260 | |
| 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 990 | |
| 980 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1480 |
| Melting Onset (Solidus), °C | 1390 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 440 |
| Thermal Conductivity, W/m-K | 15 | |
| 11 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.1 | |
| 1.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.5 | |
| 1.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 19 | |
| 75 |
| Density, g/cm3 | 7.8 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 3.7 | |
| 13 |
| Embodied Energy, MJ/kg | 52 | |
| 190 |
| Embodied Water, L/kg | 150 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 160 | |
| 240 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 | |
| 300 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 20 | |
| 28 |
| Strength to Weight: Bending, points | 19 | |
| 24 |
| Thermal Diffusivity, mm2/s | 4.1 | |
| 2.8 |
| Thermal Shock Resistance, points | 16 | |
| 24 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.35 |
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.030 |
| Chromium (Cr), % | 18 to 20 | |
| 19 to 22 |
| Iron (Fe), % | 61.7 to 70.9 | |
| 0 to 11.3 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 to 0.2 |
| Molybdenum (Mo), % | 2.0 to 2.5 | |
| 7.0 to 9.5 |
| Nickel (Ni), % | 9.0 to 12 | |
| 59 to 63 |
| Niobium (Nb), % | 0 | |
| 2.8 to 4.0 |
| Nitrogen (N), % | 0.12 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 1.5 | |
| 0 to 0.2 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 1.0 to 1.6 |