EN 1.4501 Stainless Steel vs. EN 1.4017 Stainless Steel

Both EN 1.4501 stainless steel and EN 1.4017 stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4501 stainless steel and the bottom bar is EN 1.4017 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 27
14
Fatigue Strength, MPa 430
220
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
77
Shear Strength, MPa 540
350
Tensile Strength: Ultimate (UTS), MPa 830
580
Tensile Strength: Yield (Proof), MPa 600
390

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 450
410
Maximum Temperature: Mechanical, °C 1100
870
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1410
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
30
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 22
9.5
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.1
2.2
Embodied Energy, MJ/kg 57
31
Embodied Water, L/kg 180
120

Common Calculations

PREN (Pitting Resistance) 42
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
71
Resilience: Unit (Modulus of Resilience), kJ/m3 870
380
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 29
21
Strength to Weight: Bending, points 25
20
Thermal Diffusivity, mm2/s 4.0
8.1
Thermal Shock Resistance, points 22
20

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 24 to 26
16 to 18
Copper (Cu), % 0.5 to 1.0
0
Iron (Fe), % 57.6 to 65.8
78.3 to 82.8
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 3.0 to 4.0
0
Nickel (Ni), % 6.0 to 8.0
1.2 to 1.6
Nitrogen (N), % 0.2 to 0.3
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015
Tungsten (W), % 0.5 to 1.0
0