EN 1.4510 Stainless Steel vs. SAE-AISI 8822 Steel

Both EN 1.4510 stainless steel and SAE-AISI 8822 steel are iron alloys. Both are furnished in the annealed condition. They have 83% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4510 stainless steel and the bottom bar is SAE-AISI 8822 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 26
23
Fatigue Strength, MPa 190
270
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Shear Strength, MPa 330
340
Tensile Strength: Ultimate (UTS), MPa 510
540
Tensile Strength: Yield (Proof), MPa 270
370

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 870
420
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
38
Thermal Expansion, µm/m-K 11
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 3.4
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 8.5
2.8
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.2
1.6
Embodied Energy, MJ/kg 32
21
Embodied Water, L/kg 120
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
110
Resilience: Unit (Modulus of Resilience), kJ/m3 180
360
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 18
19
Strength to Weight: Bending, points 18
19
Thermal Diffusivity, mm2/s 6.7
10
Thermal Shock Resistance, points 17
18

Alloy Composition

Carbon (C), % 0 to 0.050
0.2 to 0.25
Chromium (Cr), % 16 to 18
0.4 to 0.6
Iron (Fe), % 79.1 to 83.9
96.6 to 97.8
Manganese (Mn), % 0 to 1.0
0.75 to 1.0
Molybdenum (Mo), % 0
0.3 to 0.4
Nickel (Ni), % 0
0.4 to 0.7
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.015
0 to 0.040
Titanium (Ti), % 0.15 to 0.8
0