EN 1.4513 Stainless Steel vs. EN 1.7225 Steel

Both EN 1.4513 stainless steel and EN 1.7225 steel are iron alloys. They have 82% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4513 stainless steel and the bottom bar is EN 1.7225 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
73
Tensile Strength: Ultimate (UTS), MPa 480
540 to 1850

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 880
420
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 25
46
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.9
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 10
2.5
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.5
1.5
Embodied Energy, MJ/kg 35
20
Embodied Water, L/kg 120
51

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
19 to 65
Strength to Weight: Bending, points 18
19 to 43
Thermal Diffusivity, mm2/s 6.8
12
Thermal Shock Resistance, points 17
16 to 54

Alloy Composition

Carbon (C), % 0 to 0.025
0.38 to 0.45
Chromium (Cr), % 16 to 18
0.9 to 1.2
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 77.7 to 83.1
96.6 to 98
Manganese (Mn), % 0 to 1.0
0.6 to 0.9
Molybdenum (Mo), % 0.8 to 1.4
0.15 to 0.3
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.035
Titanium (Ti), % 0.15 to 0.8
0